5000, 6000, and 7000 series aluminium extrusion manufacturing: EN AW-5083, 5754, 6060, 6063, 6005A, 6082, 6463, 7020, and 7075 produced with either PREMIUM or Secondary billet.
Chemical composition (EN 573-3)
| EN AW | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti |
|---|---|---|---|---|---|---|---|---|
| EN AW-5083 | ≤ 0.40 | ≤ 0.40 | ≤ 0.10 | 0.40–1.00 | 4.00–4.90 | 0.05–0.25 | ≤ 0.25 | ≤ 0.15 |
| EN AW-5754 | ≤ 0.40 | ≤ 0.40 | ≤ 0.10 | ≤ 0.50 | 2.60–3.60 | ≤ 0.30 | ≤ 0.20 | ≤ 0.15 |
| EN AW-6060 | 0.30–0.60 | 0.10–0.30 | ≤ 0.10 | ≤ 0.10 | 0.35–0.60 | ≤ 0.05 | ≤ 0.15 | ≤ 0.10 |
| EN AW-6063 | 0.20–0.60 | ≤ 0.35 | ≤ 0.10 | ≤ 0.10 | 0.45–0.90 | ≤ 0.10 | ≤ 0.10 | ≤ 0.10 |
| EN AW-6005A | 0.50–0.90 | ≤ 0.35 | ≤ 0.30 | ≤ 0.50 | 0.40–0.70 | ≤ 0.30 | ≤ 0.20 | ≤ 0.10 |
| EN AW-6082 | 0.70–1.30 | ≤ 0.50 | ≤ 0.10 | 0.40–1.00 | 0.60–1.20 | ≤ 0.25 | ≤ 0.20 | ≤ 0.10 |
| EN AW-6463 | 0.20–0.60 | ≤ 0.15 | ≤ 0.20 | ≤ 0.05 | 0.45–0.90 | ≤ 0.05 | ≤ 0.05 | ≤ 0.15 |
| EN AW-7020 | ≤ 0.35 | ≤ 0.40 | ≤ 0.20 | 0.05–0.50 | 1.00–1.40 | 0.10–0.35 | 4.00–5.00 | ≤ 0.20 |
| EN AW-7075 | ≤ 0.40 | ≤ 0.50 | 1.20–2.00 | ≤ 0.30 | 2.10–2.90 | 0.18–0.28 | 5.10–6.10 | ≤ 0.20 |
Values are mass percent ranges for 5000, 6000, and 7000 series alloys; single values indicate the upper limit.
Mechanical properties (EN 755-2)
| EN AW | Temper | Rm (MPa) | Rp0,2 (MPa) | A (%) |
|---|---|---|---|---|
| EN AW-5083 | H112 | 270 | 110 | 12 |
| EN AW-5083 | H112 | 270 | 110 | 12 |
| EN AW-5754 | H112 | 190 | 80 | 14 |
| EN AW-5754 | H112 | 190 | 80 | 14 |
| EN AW-6060 | T5 | 160 | 120 | 8 |
| EN AW-6060 | T6 | 190 | 150 | 8 |
| EN AW-6060 | T66 | 215 | 170 | 8 |
| EN AW-6063 | T5 | 160 | 110 | 8 |
| EN AW-6063 | T6 | 205 | 170 | 8 |
| EN AW-6063 | T66 | 245 | 200 | 8 |
| EN AW-6005A | T5 | 260 | 215 | 8 |
| EN AW-6005A | T6 | 290 | 250 | 8 |
| EN AW-6082 | T5 | 270 | 230 | 8 |
| EN AW-6082 | T6 | 290 | 250 | 8 |
| EN AW-6463 | T5 | 150 | 110 | 8 |
| EN AW-6463 | T6 | 195 | 160 | 8 |
| EN AW-7020 | T6 | 350 | 290 | 10 |
| EN AW-7075 | T6 | 530 | 460 | 7 |
Values are minimums for wall thickness up to 5 mm and decrease as the section gets thicker.
Temper, raw material and finish
Manufactured in H112, T5, T6, and T66 tempers using PREMIUM or Secondary billet; EN AW-6463 is selected for bright anodizing and 7000 series (7020, 7075) for defense and high-strength applications.
Request a quote
EN 573-3 chemical composition and EN 755-2 mechanical property tables for EN AW-5083, 5754, 6060, 6063, 6005A, 6082, 6463, 7020 and 7075 extrusion alloys.